Carbon fiber reinforced (30%) and high flow Polyetheretherketone (PEEK)
VESTAKEEP® 2000CF30 is high flow fiber PEEK with 30% carbon fiber mainly for injection molding.
This grade has high mechanical strength, excellent heat and chemical resistance and its molded products are flame retardant.
This grade can be processed by general injection molding machine,
We recommend a high-temperature molding machine with a temperature of 400ºC or higher.
The mold temperature is recommended in the temperature range of 180-200ºC (preferably 200ºC).
This grade is supplied as pellets in a 25kg box with a polyethylene liner.
The quality guarantee period is separately specified.
| Applications | Automotive, Aerospace, General Industries, Sports ＆ Lifestyle |
|---|---|
| Molding Methods | Injection molding |
| Color | |
| Shapes | Granules |
| Characteristics | High Heat Resistance, High Rigidity, CF (Carbon Fiber) Reinforced, Conduction, Flame Retardant, High Flow |
Property
| Items | Condition | Test Method | Unit | VESTAKEEP® 2000CF30 |
|---|---|---|---|---|
| Melting point | - | ISO 11357-3 | ℃ | 340 |
| MVR | 190℃, 2.16kg | ISO 1133 | cm3/10min | - |
| 230℃, 2.16kg | cm3/10min | - | ||
| Tensile modulus | 23℃50%Rh | ISO 527-1,2 | MPa | 24,0 |
| Tensile stress at yield | MPa | - | ||
| Elongation at yield | % | - | ||
| Flexural modulus | ISO 178 | MPa | 21,500 | |
| Flexural strength | MPa | 390 | ||
| CHARPY impact strength (23℃) | ISO 179/1eA | kJ/m2 | 51C | |
| CHARPY impact strength (-30℃) | kJ/m2 | 45C | ||
| CHARPY notched impact strength (23℃) | kJ/m2 | 8C | ||
| CHARPY notched impact strength (-30℃) | kJ/m2 | 8C | ||
| Shore D hardness | - | ISO 868 | - | 90 |
| Heat deflection temperature | 1.8MPa | ISO 75-1,2 | ℃ | 330 |
| 0.45MPa | ℃ | 340 | ||
| Relative permittivity | 23℃, 100Hz | IEC 62631-2-1 | - | - |
| 23℃, 1MHz | - | 17 | ||
| Dissipation factor | 23℃, 100Hz | 10-4 | - | |
| 23℃, 1MHz | 10-4 | 2,300 |